SBRS-(4X)GR2000

SBRS-(4X)GR2000
Flame-Retardant, High Viscosity,Adhesive-Lined, Semi-rigid Polyolefin Heat Shrink Tubing
It consists of a double layer of cross-linked polyolefin and polyamide PA. Widely used in automotive wiring harness, electronic equipment wire connection and other sealed occasions.
Technical Data
It consists of a double layer of cross-linked polyolefin and polyamide PA. Widely used in automotive wiring harness, electronic equipment wire connection and other sealed occasions.

Features
- 4:1 shrink ratio to cover varying splice configurations and substrate profiles
- Flame-retardant and mechanically tough, providing strain relief and abrasion protection for wire splices, terminals, and other components
- Thick adhesive liner forms an effective barrier against fluids and moisture penetration
- Minimum shrink temperature: 110°C [230°F]
- Continuous operating temperature: -40°C to 130°C [-40°F to 266°F]
- Fully shrink temperature: 135℃ [275°F]
- Can be applied for multiple strands wire sealing
Technical Data
Property | Test Method | Standard |
---|---|---|
Tensile Strength (MPa) | ASTM D2671 | ≥10.3 |
Elongation (%) | ASTM D2671 | ≥250 |
Heat Shock 4 hours at 250±3℃ | ASTM D2671 | No dropping, flowing, or cracking |
Flammability | ASTM D2671 B | Self-extinguishing within 30 seconds |
2% Secant Modulus (expanded, MPa) | ASTM D2671 | ≥173 |
Dielectric Strength (kV/mm) | IEC 243 | ≥15 |
Volume Resistivity (Ω.cm) | ASTM D876 | ≥1×1013 |
*Calculate based on wall thickness of jacket only.
Adhesive
Property | Test Method | Standard |
---|---|---|
Water Absorption | ASTM D570 | <0.2% |
Softening Point (℃) | ASTM E28 | 100±5 |
Strength of Peeling (PE) | ASTM D 1000 | 120N/25mm |
Strength of Peeling (AL) | ASTM D 1000 | 80N/25mm |
Specification Table
DimensionsSize | Expanded | After Recovery | ||
mm |
Inner Diameter Min(mm) |
Inner Diameter Max(mm) |
Total Wall Thickness(mm) |
Adhesive Thickness(mm) |
Φ5.72 |
5.72 |
1.27 |
1.42 |
0.65 |
Φ7.44 |
7.44 |
1.65 |
1.76 |
0.90 |
Φ10.85 |
10.85 |
2.41 |
2.10 |
1.20 |
​​Φ17.78 |
17.78 |
4.45 |
2.41 |
1.37 |
*Wall thickness will be less if tubing recovery is restricted during shrinkage.