SBRS-(4X)GRH

SBRS-(4X)GRH
High-Shrink-Ratio, High Temperature Resistant, Adhesive-Lined ,Polyolefin Heat Shrink Tubing
It consists of a double layer of cross-linked polyolefin and polyamide PA. The product has high shrinkage and wear resistance characteristics, and is widely used in high temperatureenvironments such as wiring harnesses inside automotive engine compartments, electrical connections to electronic equipment, and other occasions where sealing is required.
Technical Data
It consists of a double layer of cross-linked polyolefin and polyamide PA. The product has high shrinkage and wear resistance characteristics, and is widely used in electronic equipment wiring connections, automotive harnesses, home appliance harnesses, wire and cable branches, metal pipelines, wire and cable repairs, and other occasions that require sealing.

Features
- 4:1 shrink ratio allows for fewer sizes to cover numerous splice configurations and diameters
- Hot melt adhesive made of polyamide (PA) material with high temperature resistance (no dripping at 125℃), strong permeability, and strong sealing performance
- Thick adhesive liner forms an effective barrier against fluids and moisture penetration
- Minimum shrink temperature: 70°C
- Continuous operating temperature: -45°C to 125°C
- Fully shrink temperature: 125℃
- Standard color: black, clear (other colors can be customized)
Technical Data
Property | Test Method | Standard |
---|---|---|
Tensile Strength (MPa) | ASTM D2671 | ≥10.4 |
Elongation (%) | ASTM D2671 | ≥200 |
Tensile Strength after Aging (MPa) | ASTM D2671 (158℃×168h) | ≥7.3 |
Elongation after Aging (%) | ASTM D2671 (158℃×168h) | ≥100 |
Dielectric Strength (kV/mm) | IEC 60243 | ≥15 |
Volume Resistivity (Ω·cm) | ASTM D876 | ≥1×1014 |
Adhesive
Property | Test Method | Standard |
---|---|---|
Water Absorption | ASTM D570 | <0.2% |
Softening Point (℃) | ASTM E28 | 95±5 |
Strength of Peeling (PE) | ASTM D 1000 | 120N/25mm |
Strength of Peeling (AL) | ASTM D 1000 | 80N/25mm |
Specification Table
DimensionsSize | Expanded | After Recovery | ||
mm |
Inner Diameter Min(mm) |
Inner Diameter Max(mm) |
Total Wall Thickness(mm) |
Adhesive Thickness(mm) |
Φ4.00 |
4.00 |
0.95 |
1.40±0.30 |
0.70±0.20 |
Φ5.75 |
5.75 |
1.27 |
1.70±0.30 |
0.80±0.20 |
Φ7.40 |
7.40 |
1.65 |
2.00±0.30 |
0.95±0.20 |
Φ10.80 |
10.80 |
2.00 |
2.30±0.40 |
1.10±0.20 |
Φ12.00 |
12.00 |
2.41 |
2.45±0.40 |
1.20±0.20 |
Φ14.00 |
14.00 |
3.50 |
2.50±0.40 |
1.20±0.30 |
​Φ17.78 |
17.80 |
4.20 |
2.60±0.40 |
1.35±0.30 |
*Wall thickness will be less if tubing recovery is restricted during shrinkage.