WRSBG
WRSBG
Heat Shrink Semi-conductive Tube
Manufactured from cross linked semi-conductive polyolefin. Shrink temperature: start at 90℃, and fully recovered at 130℃. Color: black.
Technical Data
| Property | Test Method | Standard Value |
| Tensile Strength | ASTM-D-638 | ≥10MPa |
| Elongation at Break | ASTM-D-638 | ≥350% |
|
Tensile Strength Variation After Heat Aging（130℃x168h） |
ASTM-D-5510 | ≤±20% |
|
Elongation at Break Variation After Heat Aging（130℃x168h） |
ASTM-D-5510 | ≤±20% |
| Volume Resistivity | IEC 60093 | ≥1x103Ω.cm |
| Hardness（Shore A） | ISO 868 | ≥80 |
| Heat Shock | 160℃，4h | No Crack |
| Brittle Temperature | ISO 974 | -40℃ |
| Longitudinal Shrinkage | ASTM-D-2671 | ≤10% |
| Eccentricity | ASTM-D-2671 | ≤30% |
Specification Table:
| Spec. | As Supplied/mm | After Recovered/mm |
Standard Cut Length/mm |
Standard Continuous Length (m/roll) |
||
|
Inner Diameter Min |
Wall Thickness (±0.3) |
Inner Diameter Max |
Wall Thickness (±0.3) |
|||
|
WRSBG-45/17 |
45 |
0.9 |
17 |
2.3 |
400-1200 |
25 |
|
WRSBG-50/20 |
50 |
0.9 |
20 |
2.3 |
400-1200 |
25 |
| WRSBG-55/23 |
55 |
0.9 |
23 |
2.3 |
400-1200 |
25 |
|
WRSBG-60/24 |
60 |
0.9 |
24 |
2.3 |
400-1200 |
25 |
|
WRSBG-65/25 |
65 |
0.8 |
25 |
2.3 |
400-1200 |
25 |
|
WRSBG-75/29 |
75 |
1.0 |
29 |
2.7 |
400-1200 |
25 |
|
WRSBG-90/30 |
90 |
0.8 |
30 |
2.7 |
400-1200 |
25 |
|
WRSBG-100/36 |
100 |
0.9 |
36 |
2.7 |
400-1200 |
15 |
|
WRSBG-120/37 |
120 |
0.8 |
37 |
2.7 |
400-1200 |
15 |
| WRSBG-150/55 | 150 | 0.8 | 55 | 3.4 | 400-1200 | 15 |