| Item | Specification |
| Shrink temperature | 900C |
| Temperature range | 1250C |
| Radial shrinking ratio | ≥50% 2 : 1 |
| Longitudinal change | ≤±5% |
| Tensile strength | ≥10.4MPa |
| Ultimate elongation | ≥200% |
| Aging in circulating-air oven | 158.00C ± 1.00C, 168hrs. |
| After aging Tensile strength | ≥7.3MPa |
| After aging ultimate elongation | ≥100% |
| Volume resistivity | ≥1014Ω.cm |
| Dielectric strength at 1 min., AC2500V | No breakdown |
| Flammability | VW - 1 |
| Concentricity | ≥65% |
| Item | Specification |
| Shrink temperature | 900C |
| Temperature range | 1250C |
| Shrinking ratio | 3:1 & 4:1 |
| Longitudinal change | ≤±5% |
| Tensile strength | ≥10.4MPa |
| Ultimate elongation | ≥200% |
| Aging in circulating-air oven | 158.00C ± 1.00C, 168hrs. |
| After aging Tensile strength | ≥7.3MPa |
| After aging ultimate elongation | ≥100% |
| Volume resistivity | ≥1014Ω.cm |
| Dielectric strength at 1 min., AC2500V | No breakdown |
| Flammability | VW - 1 |
| Concentricity | ≥65% |
| Item | Specification |
| Shrink temperature | 900C |
| Operating Temperature range | -550C - 1250C |
| Radial shrinking ratio | ≥50% |
| Longitudinal change | ≤10% |
| Tensile strength | ≥10.4MPa |
| Ultimate elongation | ≥200% |
| Aging in circulating-air oven | 158.00C ± 1.00C, 168hrs. |
| After aging Tensile strength | ≥7.3MPa |
| After aging ultimate elongation | ≥100% |
| Volume resistivity | ≥1014Ω.cm |
| Dielectric strength at 1 min., AC2500V | No breakdown |
| Flammability | VW - 1 |
| Water absorption | Less than 0.4% |
| Fluid resistance | Excellent |
| Copper corrosion | No corrosion |
| Softening Point | 1200C - 50C |
| Tissue strength (N/ 25mm.) | >80 |